Ultra Thin Alminosilicate Glass Applied To Thin Triple-pane Insulated Glass Units
Thin triple-pane insulated glass units deliver high-performance glass in a thinner, more efficient manner.
These units have a much better U-value than traditional double glazing, while also solving thickness and weight issues.
Thin triple-glazed insulating glass is particularly suitable for new build and refurbishment residential applications. For new construction, its reduced weight simplifies transportation and installation.
Our CHIYAN-M2 Ultra-Clear Ultra Thin Medium Alumino-Silicate Glass is eco-friendlly alumino-silicate glass with light weight geting more and more popular in the market to improve building energy efficiency.
Features:
-
High Impact Resistance
-
High Scratch Resistance
-
Ultra High Transmittance
-
Small Warpage
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
Ultra Clear Medium Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
| Composition items | SiO₂ | Al₂O₃ | Fe₂O₃ | CaO | MgO | K₂O | Na₂O |
| Range of set value | 69.0-72.0 | 4.5-8.0 | ＜0.01 | 6.0-8.0 | 3.5-5.0 | 0.1-1.0 | 13.0-14.5 |
Physical Property Parameter
| S/N | Items | Unit | Test Standard | CY-M2 |
| 1 | Density | g/cm3 | GB/T5432-2008 | 2.48±0.01 |
| 2 | Refractive Index | / | GB/T 2680-2021 | 1.51±0.01 |
| 3 | Young's Modulus | Gpa | GB/T 37780-2019 | 73.0±0.5 |
| 4 | Transmittance | % | GB/T 2680-2021 | ≥91.5 |
| 5 | Volume Resistivity | lg(Ω .cm) | GB/T 31838.2-2019 | ≥10.0 |
| 6 | Dielectric Constant | / | SJ/T 11043-1996 | ≥7.0 |
| 7 | Softening Point | ℃ | GB/T 28195-2011 | 750±10 |
| 8 | Strain Point | ℃ | GB/T 28196-2011 | 516±5 |
| 9 | Annealing Point | ℃ | GB/T 28196-2011 | 562±5 |
| 10 | Thermal Conductivity | W/( m.K) | JC/T 675-1997 | 0.682±0.10 |
| 11 | Thermal Expansivity | * 10-7/℃ | SJ/T 11036-1996 | 85±5 |
| 12 | Photoelastic Coefficient | nm/cm/MPa | BS 7604-1-1992 | 27.0±0.2 |
| 13 | Poisson's Coefficient | / | GB/T 28195-2011 | 0.23±0.02 |
| 14 | Vickers-hardness | HV | GB/T 16534-2009 | 610±10 |
Chemical Tempering Process Parameter Setting Reference
| Technological Parameter | 400°C | 410°C | 420°C | 430°C |
| CS(MPa) | DOL(um) | CS(MPa) | DOL(um) | CS(MPa) | DOL(um) | CS(MPa) | DOL(um) |
| 3H | ≥650 | ≥7.0 | ≥650 | ≥8.0 | ≥650 | ≥9.0 | ≥650 | ≥10.5 |
| 4H | ≥600 | ≥8.0 | ≥600 | ≥9.0 | ≥600 | ≥11.0 | ≥600 | ≥12.5 |
| 5H | ≥600 | ≥9.0 | ≥600 | ≥10.0 | ≥600 | ≥11.5 | ≥600 | ≥13.0 |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Dimensions
| NO. | Item | Specification | Detection Method |
| 1 | Dimensional Tolerance | 1300*1100*(±2mm) | Tape Measure |
| 2 | Thickness | 0.50~1.1 ±0.05m 1.3~2.0 ±0.05m | Micrometer |
| 3 | Thickness Difference | ≤0.04mm | Micrometer |
| 4 | The Diagonal Difference
(Perpendicularity) | ≤0.3% | Tape Measure 
|
| 5 | Stripe | ≤Level2 | Point Sources of Light |
| 6 | Flatness (Before Tempering) | 0.50~0.55 ≤0.15%(=h/L) 0.70~2.0 ≤0.10%(=h/L) | 
|
Packing Quantity
| S/N | L*W*T(mm) | Packing Quantity (Pieces/Box) |
| 1 | 1300x1100x0.25 | 900 |
| 2 | 1300x1100x0.33 | 1020 |
| 3 | 1300x1100x0.40 | 900 |
| 4 | 1300x1100x0.50 | 750 |
| 5 | 1300x1100x0.55 | 680 |
| 6 | 1300x1100x0.70 | 550 |
| 7 | 1300x1100x0.82 | 490 |
| 8 | 1300x1100x0.95 | 420 |
| 9 | 1300x1100x1.0 | 410 |
| 10 | 1300x1100x1.1 | 370 |
| 11 | 1300x1100x1.3 | 310 |
| 12 | 1300x1100x1.5 | 280 |
| 13 | 1300x1100x1.6 | 250 |
| 14 | 1300x1100x1.8 | 230 |
| 15 | 1300x1100x2.0 | 200 |
Packaging Diagram
Storage conditions:
Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.
Product Tags:
|
|